RESUMO
Background: The bond capacity of universal adhesives should be comparable to a specific primer for zirconia. Thus, this study evaluated the bond strength to zirconia of four universal adhesives and a zirconia primer over long-term storage. Materials and Methods: The surfaces of 75 samples of zirconia were sandblasted with 50 µm aluminum oxide particles and then divided into groups (n = 15): G1 - Single Bond Universal (SBU); G2 - All Bond Universal; G3 - Peak Universal Bond; G4 - Ambar Universal (AU), and G5 - Z-Prime Plus (ZP). A cone of resin composite was constructed on the applied materials. The samples were submitted to a tensile bond strength test after 24 h using a universal testing machine. Then, the remaining materials were removed from the sample surfaces, and the surfaces were polished and sandblasted again as previously described to obtain the same groups. These new samples were stored in distilled water at 37°C for 12 months and then submitted to a tensile bond strength test. The data were analyzed by two-way analysis of variance and Tukey's test (α =0.05). Results: The material factor (P = 0.001) and the storage factor (P = 0.001) were significant, and the interaction was not significant (P = 0.117). According to Tukey's test, bond strength mean values (in MPa) followed by distinct letters were significantly different. After 24 h, G5 = 21.12 A, G1 = 20.55 A, G4 = 19.19 AB, G2 = 14.22 B, and G3 = 8.44 C. After 12 months, G1 = 7.37 A, G5 = 5.61 AB, G4 = 4.97 B, G2 = 3.32 C, and G3 = 1.93 D. After 12 months of storage, all groups' bond strength significantly decreased. Conclusions: SBU and AU had bond strengths comparable to ZP after 24 h. No material resisted water degradation.
RESUMO
The ß-ketoester benzyl acetoacetate was enantioselectively reduced to benzyl (S)-3-hydroxybutanoate by seven microorganism species. The best result using free cells was obtained with the yeast Hansenula sp., which furnished 97% ee and 85% of conversion within 24 h. After immobilization in calcium alginate spheres, K.marxianus showed to be more stable after 2 cycles of reaction.
Assuntos
Acetoacetatos/metabolismo , Compostos de Benzil/metabolismo , Kluyveromyces/metabolismo , Pichia/metabolismo , Células Imobilizadas/metabolismo , Oxirredução , Fatores de TempoRESUMO
The β-ketoester benzyl acetoacetate was enantioselectively reduced to benzyl (S)-3-hydroxybutanoate by seven microorganism species. The best result using free cells was obtained with the yeast Hansenula sp., which furnished 97% ee and 85% of conversion within 24 h. After immobilization in calcium alginate spheres, K.marxianus showed to be more stable after 2 cycles of reaction.
Assuntos
Acetoacetatos/metabolismo , Compostos de Benzil/metabolismo , Kluyveromyces/metabolismo , Pichia/metabolismo , Células Imobilizadas/metabolismo , Oxirredução , Fatores de TempoRESUMO
In this paper we report the design, synthesis and pharmacological evaluation of a series of N-phenyl-acetamide sulfonamide derivatives (5a-g), planned by structural modification on the prototype paracetamol (1). In this series (5a-g), compound LASSBio-1300 (5e; ID(50)=5.81 micromol/kg) stands out as a new non-hepatotoxic analgesic drug candidate. The increase of area, volume and electrostatic potential of paracetamol's analogues seems to be beneficial to the analgesic activity. Unlike paracetamol (1) and the other analogues (5a, 5d-g), compounds 5b and 5c presented an important anti-hypernociceptive activity associated to inflammatory pain.